DANTHANE COMPOUNDS AND COMPOUND-POWDERS

DANTHANE-COMPOUNDS (GRANULES)

Coloured special TPUs for melt calender and extrusion processing

Product name

Description

Data sheet

Safety data sheet

Applications

Manufacturing of Transportelements (Conveyor belt coating)

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A85

Density

1,23 g/cm³

Form of delivery

pearl granules

Appearance

White, RAL 9010

Melting range

150 – 160 °C

Softening range

120 – 130 °C

Glass transition temperature

-28 °C

Tensile strength

25 MPa

Approvals

FDA, 21CFR, §177/2600

Abrasion resistance

40 mm³

Applications

Manufacturing of Transportelements (Conveyor belt coating)

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A85

Density

1,22 g/cm³

Form of delivery

Pearl granules

Appearance

Blue RAL 5015

Melting range

135 - 145 °C

Softening range

120 - 125 °C

Glass transition temperature

-29 °C

Elongation at break

610 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

Manufacturing of Transportelements (Conveyor belt coating)

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A85

Density

1,22 g/cm³

Form of delivery

Pearl granules

Appearance

Green RAL 6005

Melting range

135 - 145 °C

Softening range

120 - 125 °C

Glass transition temperature

-30 °C

Elongation at break

620 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

Manufacturing of Transportelements (Conveyor belt coating)

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A85

Density

1,23 g/cm³

Form of delivery

Pearl granules

Appearance

Black RAL 9005

Melting range

130 - 140 °C

Softening range

125 - 130 °C

Glass transition temperature

-28 °C

Elongation at break

520 %

Tensile strength

25 MPa

Abrasion resistance

40 mm³

Applications

Coating of transport and conveyor belts, Drive elements (flat belts), Big bag materials, Container lining materials and special hoses

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A86

Functionality

High contamination resistance, very high sliding properties

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

White colored granulate (color RAL 9011)

Melting range

140 - 145 °C

Softening range

135 - 140 °C

Glass transition temperature

-27 °C

Elongation at break

500 %

Tensile strength

30 MPa

Melt flow index

65 - 95 g (190°C/10kg/10 min)

Approvals

FDA, 21CFR, §177/2600

Abrasion resistance

20 mm³

Applications

Melting coating of industrial textiles

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A94

Density

1,23 g/cm³

Form of delivery

Granules

Appearance

White evenly colored pearl granules (RAL 9010)

Melting range

155 – 165 °C

Softening range

140 – 150 °C

Glass transition temperature

-23 °C

Elongation at break

450 %

Tensile strength

30 MPa

Approvals

FDA, 21CFR, §177/2600

Abrasion resistance

60 mm³

Applications

Melting coating of industrial textiles

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A94

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

Blue evenly colored pearl granules (RAL 5015)

Melting range

165 - 175 °C

Softening range

140 - 160 °C

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190°C/10,0kg/10 min)

Abrasion resistance

40 mm³

Applications

Melting coating of industrial textiles

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

Green evenly colored pearl granules (RAL 6005)

Melting range

165 - 175 °C

Softening range

140 - 160 °C

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190°C/10,0kg/10 min)

Abrasion resistance

40 mm³

Applications

Melting coating of industrial textiles

Polymer

Polyester-TPU

Processing

Extrusion, calender

Chemical structure

Aromatic

Hardness

A96

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

Black evenly colored pearl granules (RAL 9005)

Melting range

160 – 170 °C

Softening range

145 - 155 °C

Glass transition temperature

-25 °C

Elongation at break

420 %

Tensile strength

35 MPa

Approvals

FDA, 21CFR, §177/2600

Abrasion resistance

35 mm³

FUNCTIONAL COMPOUNDS (GRANULES)

Functional TPU compounds for special applications

Product name

Description

Data sheet

Safety data sheet

Applications

Foil fabric coatings, electrically conductive shoe components, Various plastic injection molded parts

Polymer

Polyester-TPU

Processing

Calender, extrusion, injection molding

Chemical structure

aromatic

Hardness

A85

Functionality

Electric conductivity 120 – 190 KΩ

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

black pearl granules

Melting range

155 – 165 °C

Softening range

130 – 145 °C

Elongation at break

500 %

Tensile strength

30 MPa

Melt flow index

50 - 70g (10 Min/220°C/10kg)

Abrasion resistance

25 mm³

Applications

Electrically conductive or antistatic TPU-Films

Polymer

Polyester-TPU

Processing

Calender, extrusion, injection molding

Chemical structure

aromatic

Hardness

A92

Functionality

Electric conductivity 120 – 190 KΩ

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

black pearl granules

Melting range

175 bis 185 °C

Softening range

160 bis 165°C

Elongation at break

430 %

Tensile strength

40 MPa

Melt flow index

50 - 70g (10 Min/220°C/10kg)

Abrasion resistance

28 mm³

Applications

Coating of conveyor belts, drive elements (flat belts), Big Bag Materials, container lining materials and special hoses

Polymer

Polyester-TPU

Processing

Calender, extrusion,

Chemical structure

aromatic

Hardness

A86

Functionality

high dirt resistance and very high lubricity

Density

1,20 g/cm³

Form of delivery

Granules

Appearance

White colored granules

Melting range

140 - 145 °C

Softening range

135 - 140 °C

Glass transition temperature

-27 °C

Elongation at break

500 %

Tensile strength

30 MPa

Melt flow index

65 - 95 g (190°C/10kg/10 min)

Approvals

FDA, 21CFR, §177/2600

Abrasion resistance

20 mm³

Applications

Components in the vehicle interior

Polymer

Polycaprolacton-Copolyester

Processing

Extrusion, injection molding

Chemical structure

aromatic

Hardness

A93

Density

1,17 g/cm³

Appearance

Schwarz (RAL 9005)

Melting range

184 – 194 °C

Softening range

175 – 185 °C

Glass transition temperature

-34 °C

Elongation at break

560 %

Tensile strength

42 MPa

Melt flow index

55- 90g (220°C/3,80kg/10 min)

Abrasion resistance

25 mm³

DANTHANE-POWDER

  • Special powders based on TPU
  • Areas of application:
    • Sintering coating
    • Paste dot coating
    • Doubble-point coating
    • Powder dot coating
    • Powder impregnation
    • Flatbed lamination
    • Transfer calender lamination

Product name

Description

Data sheet

Safety data sheet

Applications

Dot point coating of textiles, nonwovens and other carrier materials

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,20 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Transparent

Melting range

135 - 145 °C

Softening range

135 - 145 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-27 °C

Elongation at break

500 %

Tensile strength

30 MPa

Abrasion resistance

25 mm³

Applications

Coating of transport elements (transport and conveyor belt textiles) as well as for coating of flat belts, flexible containers and technical textiles

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,23 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

White colored TPU powder (colour RAL 9010)

Melting range

140 - 150°C

Softening range

135 - 145 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-28 °C

Elongation at break

520 %

Tensile strength

25 MPa

Abrasion resistance

40 mm³

Applications

Manufacturing of blue coloured transport elements (Transport and conveyor belts) as well as flat belt and flexible container material

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,22 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Blue colored TPU powder (Farbe RAL 5015)

Melting range

135 – 145 °C

Softening range

120 – 130 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-29 °C

Elongation at break

610 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

Manufacturing of green coloured transport elements (transport- and conveyor belt textile coating)

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,22 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Green colored TPU powder (colour RAL 6005)

Melting range

135 – 145 °C

Softening range

125 – 130 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-30 °C

Elongation at break

620 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

Manufacturing of green coloured transport elements (transport- and conveyor belt textile coating)

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,22 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

White-green colored TPU powder (Farbe: RAL 6019)

Melting range

135 – 145 °C

Softening range

125 – 130 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-30 °C

Elongation at break

620 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

Manufacturing of black coloured transport elements (transport- and conveyor belt textile coating)

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A85

Density

1,23 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Black colored TPU powder (colour RAL 9005)

Melting range

130 – 140 °C

Softening range

120 – 130 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Glass transition temperature

-28 °C

Elongation at break

520 %

Tensile strength

25 MPa

Abrasion resistance

30 mm³

Applications

sinter coating of technical textiles

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,20 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Melting range

165 – 175 °C

Softening range

140 – 160 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190 °C/10 kg/10 min)

Abrasion resistance

25 mm³

Applications

Sinter coating of technical textiles

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,20 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

White powder (Farbe RAL 9010)

Melting range

165 – 175 °C

Softening range

140 – 160 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190 °C/10 kg/10 min)

Abrasion resistance

25 mm³

Applications

Sinter coating of technical textiles

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,20 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Blue powder (Farbe RAL 5015)

Melting range

165 – 175 °C

Softening range

140 – 160 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190 °C/10 kg/10 min)

Abrasion resistance

25 mm³

Applications

Sinter coating of technical textiles; manufacturing of conveyor belts; coating of flat belt materials

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,20 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Green powder (Farbe RAL 6005)

Melting range

165 – 175 °C

Softening range

140 – 160 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Elongation at break

420 %

Tensile strength

35 MPa

Melt flow index

65 - 95 g (190 °C/10 kg/10 min)

Abrasion resistance

25 mm³

Applications

Sinter coating of technical textiles; manufacturing of conveyor belts; coating of flat belt materials

Polymer

Polyester-TPU

Chemical structure

Aromatic

Hardness

A94 / D36

Density

1,23 g/cm³

Other properties

Standard powder grain size 50-500μ

Form of delivery

Powder

Appearance

Black powder (Farbe RAL 9005)

Melting range

165 – 170 °C

Softening range

140 – 160 °C

Resistance

Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons

Elongation at break

420 %

Tensile strength

35 MPa

Abrasion resistance

25 mm³