Danthane Compounds and Compound-Powders
DANTHANE-Compounds (Granules)
Coloured special TPUs for melt calender and extrusion processing
Product name
Description
Data sheet
Safety data sheet
Applications
Manufacturing of Transportelements (Conveyor belt coating)
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A85
Density
1,23 g/cm³
Form of delivery
pearl granules
Appearance
White, RAL 9010
Melting range
150 – 160 °C
Softening range
120 – 130 °C
Glass transition temperature
-28 °C
Tensile strength
25 MPa
Approvals
FDA, 21CFR, §177/2600
Abrasion resistance
40 mm³
Applications
Manufacturing of Transportelements (Conveyor belt coating)
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A85
Density
1,22 g/cm³
Form of delivery
Pearl granules
Appearance
Blue RAL 5015
Melting range
135 - 145 °C
Softening range
120 - 125 °C
Glass transition temperature
-29 °C
Elongation at break
610 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
Manufacturing of Transportelements (Conveyor belt coating)
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A85
Density
1,22 g/cm³
Form of delivery
Pearl granules
Appearance
Green RAL 6005
Melting range
135 - 145 °C
Softening range
120 - 125 °C
Glass transition temperature
-30 °C
Elongation at break
620 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
Manufacturing of Transportelements (Conveyor belt coating)
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A85
Density
1,23 g/cm³
Form of delivery
Pearl granules
Appearance
Black RAL 9005
Melting range
130 - 140 °C
Softening range
125 - 130 °C
Glass transition temperature
-28 °C
Elongation at break
520 %
Tensile strength
25 MPa
Abrasion resistance
40 mm³
Applications
Coating of transport and conveyor belts, Drive elements (flat belts), Big bag materials, Container lining materials and special hoses
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A86
Functionality
High contamination resistance, very high sliding properties
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
White colored granulate (color RAL 9011)
Melting range
140 - 145 °C
Softening range
135 - 140 °C
Glass transition temperature
-27 °C
Elongation at break
500 %
Tensile strength
30 MPa
Melt flow index
65 - 95 g (190°C/10kg/10 min)
Approvals
FDA, 21CFR, §177/2600
Abrasion resistance
20 mm³
Applications
Melting coating of industrial textiles
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A94
Density
1,23 g/cm³
Form of delivery
Granules
Appearance
White evenly colored pearl granules (RAL 9010)
Melting range
155 – 165 °C
Softening range
140 – 150 °C
Glass transition temperature
-23 °C
Elongation at break
450 %
Tensile strength
30 MPa
Approvals
FDA, 21CFR, §177/2600
Abrasion resistance
60 mm³
Applications
Melting coating of industrial textiles
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A94
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
Blue evenly colored pearl granules (RAL 5015)
Melting range
165 - 175 °C
Softening range
140 - 160 °C
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190°C/10,0kg/10 min)
Abrasion resistance
40 mm³
Applications
Melting coating of industrial textiles
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
Green evenly colored pearl granules (RAL 6005)
Melting range
165 - 175 °C
Softening range
140 - 160 °C
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190°C/10,0kg/10 min)
Abrasion resistance
40 mm³
Applications
Melting coating of industrial textiles
Polymer
Polyester-TPU
Processing
Extrusion, calender
Chemical structure
Aromatic
Hardness
A96
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
Black evenly colored pearl granules (RAL 9005)
Melting range
160 – 170 °C
Softening range
145 - 155 °C
Glass transition temperature
-25 °C
Elongation at break
420 %
Tensile strength
35 MPa
Approvals
FDA, 21CFR, §177/2600
Abrasion resistance
35 mm³
Functional Compounds (Granules)
Functional TPU compounds for special applications
Product name
Description
Data sheet
Safety data sheet
Applications
Foil fabric coatings, electrically conductive shoe components, Various plastic injection molded parts
Polymer
Polyester-TPU
Processing
Calender, extrusion, injection molding
Chemical structure
aromatic
Hardness
A85
Functionality
Electric conductivity 120 – 190 KΩ
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
black pearl granules
Melting range
155 – 165 °C
Softening range
130 – 145 °C
Elongation at break
500 %
Tensile strength
30 MPa
Melt flow index
50 - 70g (10 Min/220°C/10kg)
Abrasion resistance
25 mm³
Applications
Electrically conductive or antistatic TPU-Films
Polymer
Polyester-TPU
Processing
Calender, extrusion, injection molding
Chemical structure
aromatic
Hardness
A92
Functionality
Electric conductivity 120 – 190 KΩ
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
black pearl granules
Melting range
175 bis 185 °C
Softening range
160 bis 165°C
Elongation at break
430 %
Tensile strength
40 MPa
Melt flow index
50 - 70g (10 Min/220°C/10kg)
Abrasion resistance
28 mm³
Applications
Coating of conveyor belts, drive elements (flat belts), Big Bag Materials, container lining materials and special hoses
Polymer
Polyester-TPU
Processing
Calender, extrusion,
Chemical structure
aromatic
Hardness
A86
Functionality
high dirt resistance and very high lubricity
Density
1,20 g/cm³
Form of delivery
Granules
Appearance
White colored granules
Melting range
140 - 145 °C
Softening range
135 - 140 °C
Glass transition temperature
-27 °C
Elongation at break
500 %
Tensile strength
30 MPa
Melt flow index
65 - 95 g (190°C/10kg/10 min)
Approvals
FDA, 21CFR, §177/2600
Abrasion resistance
20 mm³
Applications
Components in the vehicle interior
Polymer
Polycaprolacton-Copolyester
Processing
Extrusion, injection molding
Chemical structure
aromatic
Hardness
A93
Density
1,17 g/cm³
Appearance
Schwarz (RAL 9005)
Melting range
184 – 194 °C
Softening range
175 – 185 °C
Glass transition temperature
-34 °C
Elongation at break
560 %
Tensile strength
42 MPa
Melt flow index
55- 90g (220°C/3,80kg/10 min)
Abrasion resistance
25 mm³
DANTHANE-Powder
- Special powders based on TPU
- Areas of application:
- Sintering coating
- Paste dot coating
- Doubble-point coating
- Powder dot coating
- Powder impregnation
- Flatbed lamination
- Transfer calender lamination
Product name
Description
Data sheet
Safety data sheet
Applications
Dot point coating of textiles, nonwovens and other carrier materials
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,20 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Transparent
Melting range
135 - 145 °C
Softening range
135 - 145 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-27 °C
Elongation at break
500 %
Tensile strength
30 MPa
Abrasion resistance
25 mm³
Applications
Coating of transport elements (transport and conveyor belt textiles) as well as for coating of flat belts, flexible containers and technical textiles
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,23 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
White colored TPU powder (colour RAL 9010)
Melting range
140 - 150°C
Softening range
135 - 145 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-28 °C
Elongation at break
520 %
Tensile strength
25 MPa
Abrasion resistance
40 mm³
Applications
Manufacturing of blue coloured transport elements (Transport and conveyor belts) as well as flat belt and flexible container material
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,22 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Blue colored TPU powder (Farbe RAL 5015)
Melting range
135 – 145 °C
Softening range
120 – 130 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-29 °C
Elongation at break
610 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
Manufacturing of green coloured transport elements (transport- and conveyor belt textile coating)
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,22 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Green colored TPU powder (colour RAL 6005)
Melting range
135 – 145 °C
Softening range
125 – 130 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-30 °C
Elongation at break
620 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
Manufacturing of green coloured transport elements (transport- and conveyor belt textile coating)
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,22 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
White-green colored TPU powder (Farbe: RAL 6019)
Melting range
135 – 145 °C
Softening range
125 – 130 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-30 °C
Elongation at break
620 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
Manufacturing of black coloured transport elements (transport- and conveyor belt textile coating)
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A85
Density
1,23 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Black colored TPU powder (colour RAL 9005)
Melting range
130 – 140 °C
Softening range
120 – 130 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Glass transition temperature
-28 °C
Elongation at break
520 %
Tensile strength
25 MPa
Abrasion resistance
30 mm³
Applications
sinter coating of technical textiles
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,20 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Melting range
165 – 175 °C
Softening range
140 – 160 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190 °C/10 kg/10 min)
Abrasion resistance
25 mm³
Applications
Sinter coating of technical textiles
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,20 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
White powder (Farbe RAL 9010)
Melting range
165 – 175 °C
Softening range
140 – 160 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190 °C/10 kg/10 min)
Abrasion resistance
25 mm³
Applications
Sinter coating of technical textiles
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,20 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Blue powder (Farbe RAL 5015)
Melting range
165 – 175 °C
Softening range
140 – 160 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190 °C/10 kg/10 min)
Abrasion resistance
25 mm³
Applications
Sinter coating of technical textiles; manufacturing of conveyor belts; coating of flat belt materials
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,20 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Green powder (Farbe RAL 6005)
Melting range
165 – 175 °C
Softening range
140 – 160 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Elongation at break
420 %
Tensile strength
35 MPa
Melt flow index
65 - 95 g (190 °C/10 kg/10 min)
Abrasion resistance
25 mm³
Applications
Sinter coating of technical textiles; manufacturing of conveyor belts; coating of flat belt materials
Polymer
Polyester-TPU
Chemical structure
Aromatic
Hardness
A94 / D36
Density
1,23 g/cm³
Other properties
Standard powder grain size 50-500μ
Form of delivery
Powder
Appearance
Black powder (Farbe RAL 9005)
Melting range
165 – 170 °C
Softening range
140 – 160 °C
Resistance
Good resistance to oils, petrol, ester, ketone and chlorinated hydrocarbons
Elongation at break
420 %
Tensile strength
35 MPa
Abrasion resistance
25 mm³