Danpol

Applications

Coatings with food contact, Sterilizable coatings, Deep-drawable coil, strip and metal coatings, Can coatings

Polymer

Copolyester

Processing

In solvent or extrusion

Solid content

100 %

Density

1,20 g/cm³

Other properties

Very good adhesion to metals

Form of delivery

Granule

Appearance

Transparent, whitish

Softening range

128 °C (R&B)

Solubility

various solvents

Glass transition temperature

~35 °C

Approvals

food packaging

Hydroxyl value

<9 mg KOH/g

Acid value

<3 mg KOH/g

Applications

Heat-activated adhesives, heat-seal varnishes, primers, adhesion promoters

Polymer

Copolyester

Processing

In solvent or extrusion

Functionality

excellent green tack and long open time

Solid content

100 %

Density

1,20 g/cm³

Other properties

very good adhesion to metals, as well as to the different textile and plastic materials

Form of delivery

Granules

Appearance

transparent, milky

Softening range

130 °C (R&B)

Solubility

various solvents, e.g. ethyl acetat, MEK, acetone

Glass transition temperature

33°C

Approvals

Food contact applications; more information upon request

Hydroxyl value

< 6 mg KOH/g

Acid value

< 2 mg KOH/g

Applications

Hotmelt adhesives, Hot melt coatings, primers, solvent adhesives

Polymer

Polyester

Chemical structure

1047H

Hardness

D78

Solid content

100 %

Density

1,22 g/cm³

Other properties

Solvent viscosity: > 400 mPa.s (at 23°C solved 30% in ethylacetat)

Form of delivery

blocks

Melting range

150 °C (Kofler)

Softening range

140 °C (R&B)

Solubility

Ethyl acetate, acetone, cyclohexanone, chloroform, MEK, toluene, trichloroethane, trichloroethylene

Crystallization rate

Amorphous

Glass transition temperature

+35 °C

Elongation at break

>2000 %

Tensile strength

25-30 N/mm²

Melt viscosity

~9 Pa.s (at 232°C)

Approvals

food packaging

Hydroxyl value

4-6 mg KOH/g

Acid value

< 3 mg KOH/g

Boiling point

200°C

Applications

Coil coating coatings, laminating adhesives, film lamination, plastic coatings, primers, solvent-based adhesives

Polymer

Polyester

Viscosity

1.500 - 2.000 mPa.s (25°C)

Solid content

36-38 %

Density

1,03 g/cm³

Other properties

open time 15-25 Sek.

Form of delivery

Solution, 200kg drum

Appearance

Transparent to slightly yellowish solution

Melting range

85-90 °C (Film sample, Kofler)

Solubility

Soluble and dilutable in ketones, esters and halogenated hydrocarbons

Crystallization rate

Amorphous

Approvals

food packaging

Hydroxyl value

2 mg KOH/g

Acid value

2 mg KOH/g

Applications

Hotmelt adhesives, hotmelt coatings, primers, solvent-based adhesives

Polymer

Copolyester

Hardness

D20

Density

1,2 g/cm³

Other properties

open time 13-15 Sek.

Form of delivery

Granules

Melting range

67-77 °C (DSC, DIN 53.765)

Softening range

99°C (R&B)

Solubility

various solvents

Crystallization rate

Low

Glass transition temperature

-20 °C

Elongation at break

800%

Melt flow index

~90 g/10min (160°C)

Melt viscosity

~115 Pa.s (160°C)

Approvals

food packaging

Hydroxyl value

3-4 mg KOH/g

Acid value

< 3 mg KOH/g

Applications

Hotmelt adhesives, hotmelt coatings, primers, solvent-based adhesives

Polymer

Copolyester

Hardness

D26

Density

1,2 g/cm³

Other properties

open time 10-13 Sek.

Form of delivery

Granules

Melting range

85-95 °C (DSC, DIN 53.765)

Softening range

92°C (R&B)

Solubility

various solvents

Crystallization rate

Low

Glass transition temperature

-12 °C

Elongation at break

700%

Melt flow index

~80 g/10min (160°C)

Melt viscosity

~125 Pa.s (160°C)

Approvals

food packaging

Hydroxyl value

3-4 mg KOH/g

Acid value

< 3 mg KOH/g

Applications

Textile composites

Polymer

Copolyester

Form of delivery

Granules

Melting range

100 – 110 °C

Glass transition temperature

7,8 °C

Elongation at break

540 %

Tensile strength

200 kg/cm²

Melt viscosity

220.000 mPa.s (at 160 °C)

Applications

Textile composites

Polymer

Copolyester

Form of delivery

Granules

Melting range

110 – 120 °C

Glass transition temperature

16 °C

Elongation at break

530 %

Tensile strength

275 kg/cm²

Melt viscosity

650.000 mPa.s (at 160 °C)

Applications

Hotmelt adhesives, hotmelt coatings, primers, solvent-based adhesives

Polymer

Copolyester

Hardness

D31

Density

1,2 g/cm³

Other properties

open time 10-13 Sek.

Form of delivery

Granules

Melting range

~145 °C (DSC, DIN 53.765)

Softening range

160 °C (R&B)

Crystallization rate

High

Glass transition temperature

-30 °C

Elongation at break

500 %

Melt flow index

200 g/10min (160°C)

Melt viscosity

~9 Pa.s (232°C)

Approvals

food packaging

Hydroxyl value

3-5 mg KOH/g

Acid value

< 3 mg KOH/g

Applications

Hotmelt adhesives, Hot melt coatings, primers, solvent adhesives, powder adhesives

Polymer

Copolyester

Hardness

D55

Density

1,24 g/cm³

Other properties

open time 8-11 Sek.

Form of delivery

Granulat

Melting range

~160 °C (DSC, DIN 53.765)

Softening range

172°C (R&B)

Crystallization rate

high

Glass transition temperature

-30 °C

Elongation at break

90 %

Melt flow index

200 g/10min (180°C)

Melt viscosity

30-40 Pa.s (232°C)

Approvals

food packaging

Hydroxyl value

3-5 mg KOH/g

Acid value

< 3 mg KOH/g

Applications

Air, oil and fuel automotive filters, especially in the area of diesel fuels and bio-based fuels

Polymer

Copolyester

Density

1,25 g/cm³

Other properties

open time < 9 Sek.

Form of delivery

Granules

Melting range

145 °C (DSC)

Softening range

150 °C (R&B)

Crystallization rate

high

Melt flow index

~90 g/10min (180 °C)

Melt viscosity

~55 Pa.s (at 232 °C)

Hydroxyl value

3- 5 mg KOH/g

Acid value

< 3 mg KOH/g